1. Magnetic Test

A straightforward method for distinguishing annealed austenitic stainless steel from ferritic stainless steel is the magnetic test. Austenitic stainless steel is non-magnetic initially but may acquire slight magnetism after cold working under pressure. In contrast, pure chromium steel and low alloy steel exhibit high magnetism.

2. Nitric Acid Point Test

Stainless steel’s inherent corrosion resistance to concentrated and dilute nitric acid is a key characteristic. This resistance sets it apart from most other metals or alloys. لكن, high-carbon 420 و 440 steels may exhibit slight corrosion during nitric acid point tests, while non-ferrous metals corrode immediately upon contact with concentrated nitric acid. Dilute nitric acid poses a significant corrosion risk to carbon steel.

3. Copper Sulfate Point Test

The copper sulfate spot test offers a quick means of differentiation between ordinary carbon steel and various types of stainless steel. A 5~10% concentration of copper sulfate solution is typically used. Before conducting the test, ensure the test area is thoroughly cleaned of grease and impurities. Polish a small area with a soft grinding cloth, then apply copper sulfate solution using a dropper bottle. Ordinary carbon steel or iron will develop a surface layer of metallic copper within seconds, while stainless steel will not produce copper precipitation or exhibit copper coloration.

4. Sulfuric Acid Test

The sulfuric acid immersion test aids in distinguishing between 302/304 و 316/317 stainless steel. Begin by finely grinding the cut edge of the sample, followed by cleaning and passivation in nitric acid (2030% concentration, 6066°C temperature) for half an hour. The sulfuric acid test solution, heated to 71°C with a 10% concentration, is then used. When 302 و 304 steel are immersed, rapid corrosion occurs, generating bubbles and turning the sample black within minutes. In contrast, 316 و 317 steel exhibit minimal corrosion or slow reaction (no bubble production) and maintain their color for 10 ل 15 minutes. For increased accuracy, conduct tests on samples with known compositions simultaneously for comparison.

تيدا جانج هوا ميتال -17 سنين

إحضار المواصفات التفصيلية إلى اتصل بي اذا احتجت
لدينا جودة عالية وأسعار معقولة
📧 راشيل@tedaganghua.com
واتس اب: (+86) 138 2059 7807
أهلا في موقعنا! https://www.tedametal.com/ & https://www.teda-metal.com/ & https://www.teda-aluminum.com/